The grade 304 is widely used steel where the different grade of 304 only differs in carbon content. We manufacture the sheets or plates using 304L grade that has extra-low carbon content (0.03%). This low content causes little difference in their performance. It helps in minimizing or eliminating the carbide precipitation that occurs during the welding process. This made it excellent steel to be worked in both welded and severe corrosive environments. 304L grade steel also eliminates the need for annealing welding of joints.
This austenitic stainless steel belongs to the T-300 series of steel families. It possesses properties such as ease of fabrication, excellent corrosion resistance, and outstanding formability, making it ideal for commercial and home applications. The UNS S30403 stainless steel is used in food processing equipment, construction material, heat exchangers, nuts, bolts, woven or welded screens, and architectural molding. Since it needs no post-weld annealing thus, Stainless Steel 304L is useful in heavy gauge components.
The Stainless Steel 304L Sheets/ Plates have properties similar to that in ASTM A240/A240M. Corrosion resistance properties make it ideal to be used in corrosive media to resist cracking above 60 degrees C. The SS 304L sheets show resistance to water containing chlorides up to 200 mg/L at 60 degrees C. The UNS S30403 offers good resistance to oxidation in continuous and intermittent services at 925 degrees C and 870 degrees C, respectively. However, the user is not recommended at temperatures 425-860 degrees C.
Abhay steels have a wide variety of Stainless Steel 304L Sheets/ Plates, and our manufactured plates are known for their quality, long service life, and dimensional accuracy. The plates that we produce have excellent welding characteristics such as forming, drawing, flexibility, and spinning properties. We manufacture them from the oldest and widely used stainless steel 304L. Our manufactured products are used in different fields because we prepare them from top graded components processed by an ultra-modern processing unit. We are serving these plates since our establishment.
Our products are thus served to hundreds of customers where our selected vendors know their requirements and choices. We also have a well-connected network to dispatch our products to clients. Thus, we serve them within a frame of time committed to the clients. Moreover, we have the personnel for research and development that keep them.
For more specifications visit - SS 304L Material Properties pdf
Heat treatment
Solution treatment is done on this grade where it is heated at 1010-1120 degree C. The steel is then cool rapidly.
Welding
The Stainless Steel 304L Sheets/ Plates have excellent weldability which is done at all standard fusion methods. The welding can be done with or without the use of filler metals. Abhay steels produce polished plates, hot rolled, cold rolled, coils, strips, foils, shim sheet, chequered, perforated and circle sheet using this grade. We use grades that have dual certification which is common for both 304 and 304L. The certificates specify the grade having all chemical and mechanical properties. The finished Stainless Steel 304L Sheets/ Plates also receive certificates such as third party inspection, EN 10204/3.1B, and radiography test report.
Standards : ASTM A240 / ASME SA240
Size : 1/4" to 4"
Range : 5mm To 150mm
Thickness : 4.0mm - 100mm
Hardness : Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.
Finish : Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)
Form : Coils, Foils, Rolls, Plain Sheet, Shim Sheet, Perforated Sheet, Chequered Plate, Strip, Flats, Blank (Circle), Ring (Flange)
| Grade | UNS | DIN | JIS | EN | GOST | AFNOR |
|---|---|---|---|---|---|---|
| SS 304L | S30403 | 1.4306 / 1.4307 | SUS 304L | X2CrNi18-9 / X2CrNi19-11 | 03Х18Н11 | Z3CN18‐10 |
| Grade | C | Mn | Si | P | S | Cr | Ni |
|---|---|---|---|---|---|---|---|
| SS 304L | 0.035 max | 2.0 max | 1.0 max | 0.045 max | 0.03 max | 18 – 20 | 8 – 13 |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
|---|---|---|---|---|
| 8.0 g/cm3 | 1400 °C (2550 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
|
Grade
|
Density of ss304 in kg/m3
|
Elastic Modulus (GPa)
|
Mean Coefficient of Thermal Expansion (μm/m/°C)
|
Thermal Conductivity (W/m.K)
|
Specific Heat 0-100°C (J/kg.K)
|
Electrical Resistivity (nΩ.m)
|
|||
|
0-100°C
|
0-315°C
|
0-538°C
|
at 100°C
|
at 500°C
|
|||||
|
304/L/H
|
8000
|
193
|
17.2
|
17.8
|
18.4
|
16.2
|
21.5
|
500
|
720
|
Stainless Steel 304L Sheets Supplier | UNS S30403 Sheets | 1.4306 / 1.4307 Sheets | 304L Stainless Steel Sheet | ASTM A240 SS 304L Sheets | 304L Stainless Steel Sheet Price | Stainless Steel 304L Sheet | Stainless Steel 304L Sheets Dealer
304/304L Stainless Steel Plate | 304L Stainless Steel Plate | UNS S30403 Plates | 1.4306 / 1.4307 Plates | Stainless Steel 304L Plate | 304L Stainless Steel Plate Price | ASTM A240 SS 304L Plates | ASME SA240 Stainless Steel 304L Plates | Stainless Steel 304L Plates Stockist
Oil and Gas Pipeline | Chemical Industry | Plumbing | Water Supply Systems | Power Plant | Paper & Pulp Industry | General Purpose Applications | Fabrication Industry | Food Processing Industry | Structural Pipe
Exporter & Supplier of High Quality Stainless Steel 304L Sheets, Plates in Different Special Size and Thickness in India.